ch in this experiment the stress is raised until Hooke's Law no longer applies
Ch
the elongation becomes irreversible the metal flows
G
when the stress exceeds a certain limiting value the wire ruptures this is
called the rupture stress it depends on
details of the composition of the last the
thank yeah
Elastische Spannung
Plastische Deformation
Kraftfahrzeugexport
Metallschicht
Besprechung/Interview
Computeranimation
Elastische Spannung
Eisendraht
Besprechung/Interview
Niederspannungsnetz
Pohl, Robert Wichard
Besprechung/Interview
Wirtsgitter
Elementarteilchenphysik
Computeranimation

Metadaten

Formale Metadaten

Titel Plastic Deformation, Rupture Strength
Alternativer Titel Plastische Verformung und Zerreißfestigkeit
Serientitel The Physics Experiments of Robert Wichard Pohl (1884 - 1976)
Anzahl der Teile 62
Autor Lüders, Klaus
Pohl, Robert Otto
Beuermann, Gustav
Samwer, Konrad
Mitwirkende Stickan, Walter (Redaktion)
Lechner, Kuno (Kamera)
Gerstenberg, Thomas (Ton)
Yousefpour, Abbas (Schnitt)
Lizenz CC-Namensnennung - keine Bearbeitung 3.0 Deutschland:
Sie dürfen das Werk in unveränderter Form zu jedem legalen Zweck nutzen, vervielfältigen, verbreiten und öffentlich zugänglich machen, sofern Sie den Namen des Autors/Rechteinhabers in der von ihm festgelegten Weise nennen.
DOI 10.3203/IWF/C-14834eng
IWF-Signatur C 14834
Herausgeber IWF (Göttingen)
Erscheinungsjahr 2003
Sprache Englisch
Produzent IWF (Göttingen)
Produktionsjahr 2002

Technische Metadaten

IWF-Filmdaten Video-Clip ; F, 54 sec

Inhaltliche Metadaten

Fachgebiet Physik
Abstract The measurements performed in the experiment "Elastic deformation, Hooke's law" (C 14833) on a copper wire, which had been limited to elastic deformations at small stresses, will be extended here to larger stresses. When the yield stress is exceeded, plastic, i.e. irreversible deformation is observed. A further increase of the stress beyond the rupture strength, leads to rupture. A 40 cm long piece of wire is suspended on a lab stand, and carries a tray on which weights can be deposited. A pillow under the tray will dampen the fall when the wire ruptures. The loading of the tray occurs in three steps : First, 2 kg cause a clearly visible elongation. The addition of 1 kg results in a slow length change of several centimeters, the wire "flows", until "work hardening" leads to a constant elongation. The addition of only 200 g finally leads to rupture, as the rupture strength is exceeded.
Schlagwörter mechanics
metal physics
tension
flow stress
plastic deformation
rupture strength

Zugehöriges Material

Ähnliche Filme

Loading...